ASME/ANSI 18.16.6-10 美制全金属六角压点锁紧螺母1-1/4"-7，1"-14，7/8"-9

8,碳钢,35,蓝白锌

价格面议

起订量≥1个

运费￥0

遵循标准ASME/ANSIB 18.16.6 2017

品牌要德

库存状态-

产品规格

7/8(P9) 1(P14) 1-1/4(P7)

采购量

个

买家还在看

DIN 6927 金属六角法兰面锁紧螺母M4M5M6

面议

GB 6187.1 2型全金属六角法兰面锁紧螺母M4M5

面议

ASME/ANSI 18.16.6美制六角尼龙防松螺母1-1/4-7

面议

GB 6185.1 2型全金属六角锁紧螺母M4M5

面议

NFE27-453法标盖形螺母M8M10M12M16

面议

产品搜索

友情链接

产品详情尺寸图 3D预览图代用标准

基本参数Basic parameters

标准号ASME/ANSI B18.16.6-10

材料碳钢

性能等级8

牌号35

表面处理蓝白锌

螺纹类型美制机螺纹

头形/主体六角（双倒角）

防松顶部压点锁紧

品牌要德

单位个

材料说明

C min	0.32%	C max	0.39%	Si min	0.17%
Si max	0.37%	Mn min	0.5%	Mn max	0.8%
P max	0.35%	S max	0.35%	Cr max	0.25%
Ni max	0.3%	Cu max	0.25%	Temper point min	550℃
Temper point max	650℃	Recommended quenching piont min	830℃	Recommended quenching piont max	870℃
Normalizing point min	840℃	Normalizing point max	900℃	Tensile strength min	530MPa
Yield stress min	315MPa	Elongation after fracture min	20%	Post systolic shrinkage min	45%
Impact absorbing energy min	55J	Hardness with no heat treatment max	197HB	C min	0.32%
C max	0.39%	Si min	0.17%	Si max	0.37%
Mn min	0.5%	Mn max	0.8%	P max	0.3%
S max	0.3%	Cr max	0.25%	Ni max	0.3%
Cu max	0.25%	Normalizing point min	840℃	Normalizing point max	900℃
Recommended quenching piont min	830℃	Recommended quenching piont max	870℃	Temper point min	550℃
Temper point max	650℃	Tensile strength min	530MPa	Yield stress min	315MPa
Elongation after fracture min	20%	Post systolic shrinkage min	45%	Impact absorbing energy min	55J
Hardness with no heat treatment max	197HB	C min	0.32%	C max	0.39%
Si min	0.17%	Si max	0.37%	Mn min	0.5%
Mn max	0.8%	P max	0.25%	S max	0.2%
Cr max	0.25%	Ni max	0.3%	Cu max	0.25%
Normalizing point min	840℃	Normalizing point max	900℃	Recommended quenching piont min	830℃
Recommended quenching piont max	870℃	Temper point min	550℃	Temper point max	650℃
Tensile strength min	530MPa	Yield stress min	315MPa	Elongation after fracture min	20%
Post systolic shrinkage min	45%	Impact absorbing energy min	55J	Hardness with no heat treatment max	197HB